American Piping Products stocks A691 EFW pipe in the grades and classes listed on the following tables:
| Pipe grade | Steel type | ASTM Specification | HB, maxA | |
| Number | Grade | |||
| CM-65 | carbon-molybdenum steel | A204/A204M | A | 201 |
| CM-70 | carbon-molybdenum steel | A204/A204M | B | 201 |
| CM-75 | carbon-molybdenum steel | A204/A204M | C | 201 |
| CMSH-70 | carbon-manganese-silicon steel, normalized | A537/A537M | 1 | … |
| CMS-75 | carbon-manganese-silicon steel | A299/A299M | … | … |
| CMSH-80 | carbon-manganese-silicon steel, quenched and tempered | A537/A537M | 2 | … |
| 0.5 CR | 0.5% chromium, 0.5% molybdenum steel | A387/A387M | 2 | 201 |
| 1 CR | 1% chromium, 0.5% molybdenum steel | A387/A387M | 12 | 201 |
| 1.25 CR | 1.25% chromium, 0.5% molybdenum steel | A387/A387M | 11 | 201 |
| 2.25 CR | 2.25% chromium, 1% molybdenum steel | A387/A387M | 22 | 201 |
| 3 CR | 3% chromium, 1% molybdenum steel | A387/A387M | 21 | 201 |
| 5 CR | 5% chromium, 0.5% molybdenum steel | A387/A387M | 5 | 225 |
| 9 CR | 9% chromium 1% molybdenum steel | A387/A387M | 9 | 241 |
| 91 | 9% chromium, 1% molybdenum, vanadium, columbium | A387/A387M | 91 | 241 |
| AHardness values listed are applicable to S3. |
| Class | Heat treatment of pipe | Radiography | Pressure test |
| 10 | none | no | no |
| 11 | none | yes | no |
| 12 | none | yes | yes |
| 13 | none | no | yes |
| 20 | stress relieved | no | no |
| 21 | stress relieved | yes | no |
| 22 | stress relieved | yes | yes |
| 23 | stress relieved | no | yes |
| 30 | normalized | no | no |
| 31 | normalized | yes | no |
| 32 | normalized | yes | yes |
| 33 | normalized | no | yes |
| 40 | normalized and tempered | no | no |
| 41 | normalized and tempered | yes | no |
| 42 | normalized and tempered | yes | yes |
| 43 | normalized and tempered | none | yes |
| 50 | quenched and tempered | none | none |
| 51 | quenched and tempered | yes | none |
| 52 | quenched and tempered | yes | yes |
| 53 | quenched and tempered | none | yes |
A minimum thickness of 0.230 inch for widths over 8 to 48 inches, and 2. A minimum thickness of 0.180 inch for widths over 48 inches. Thinner material is. You may unsubscribe at any moment. For that purpose, please find our contact info in the legal notice.
Scope
| Class | Heat treatment of pipe | Radiography | Pressure test |
| 10 | none | no | no |
| 11 | none | yes | no |
| 12 | none | yes | yes |
| 13 | none | no | yes |
| 20 | stress relieved | no | no |
| 21 | stress relieved | yes | no |
| 22 | stress relieved | yes | yes |
| 23 | stress relieved | no | yes |
| 30 | normalized | no | no |
| 31 | normalized | yes | no |
| 32 | normalized | yes | yes |
| 33 | normalized | no | yes |
| 40 | normalized and tempered | no | no |
| 41 | normalized and tempered | yes | no |
| 42 | normalized and tempered | yes | yes |
| 43 | normalized and tempered | none | yes |
| 50 | quenched and tempered | none | none |
| 51 | quenched and tempered | yes | none |
| 52 | quenched and tempered | yes | yes |
| 53 | quenched and tempered | none | yes |
A minimum thickness of 0.230 inch for widths over 8 to 48 inches, and 2. A minimum thickness of 0.180 inch for widths over 48 inches. Thinner material is. You may unsubscribe at any moment. For that purpose, please find our contact info in the legal notice.
Scope
This specification covers steel pipe 16 inches in outside diameter or larger that is electric fusion welded (EFW) with filler metal added, fabricated from pressure vessel quality plate and suitable for high-pressure service at moderate temperatures. Several grades designate the type of plate used; classes designate the type of heat treatment performed during the manufacture of the pipe, whether the weld is radiographically examined, and if the pipe has been pressure tested.
Chemical composition
Product analysis of plate: The pipe manufacturer shall make an analysis of each mill heat of plate material. The product analysis shall meet the requirements of the plate specification to which the material was ordered.
Product analysis of weld: The pipe manufacturer shall make an analysis of the finished deposited weld material from each 200 feet or fraction thereof. Analysis shall conform to the welding procedure for deposited weld material. Librarian pro 4 0 – complete personal inventory systems.
Heat treatment
Classes 10, 11, 12 and 13 are not heat treated. All other classes must be heat treated according to the parameters shown below:
| Pipe grade | ASTM Specification | Post-weld heat treat temperature range (stress relieving), °F (°C) | Normalizing temperature, max unless otherwise noted, °F (°C) | Quenching temperature, max unless otherwise noted, °F (°C) | Tempering temperature, min, °F (°C) |
| CM-65 | A204/A204M | 1100-1200 (590-650) | 1700 (925) | … | … |
| CM-70 | A204/A204M | 1100-1200 (590-650) | 1700 (925) | … | … |
| CM-75 | A204/A204M | 1100-1200 (590-650) | 1700 (925) | … | … |
| CMSH-70 | A537/A537M | 1100-1200 (590-650) | 1700 (925) | … | … |
| CMS-75 | A299/A299M | 1100-1200 (590-650) | 1700 (925) | … | … |
| CMSH-80 | A537/A537M | 1100-1200 (590-650) | A | 1700 (925) | 1100-1250 (590-675) |
| 0.5 CR | A387/A387M | 1100-1300 (590-705) | 1850 (1010) | 1700 (925) | 1150-1375 (620-745) |
| 1 CR | A387/A387M | 1100-1350 (590-730) | 1850 (1010) | 1700 (925) | 1150-1375 (620-745) |
| 1.25 CR | A387/A387M | 1100-1375 (590-745) | 1850 (1010) | 1700 (925) | 1150-1375 (620-745) |
| 2.25 CR | A387/A387M | 1200-1400 (650-760) | 1850 (1010) | 1700 (925) | 1250-1400 (675-760) |
| 3 CR | A387/A387M | 1200-1400 (650-760) | 1850 (1010) | 1700 (925) | 1250-1400 (675-760) |
| 5 CR | A387/A387M | 1200-1400 (650-760) | 1850 (1010) | 1700 (925) | 1250-1400 (675-760) |
| 9 CR | A387/A387M | 1325-1375 (715-745) | B | … | 1325-1375 (715-745) |
| 91 | A387/A387M | 1350-1420 (730-770) | 1900-2000 (1040-1095) | 1900 min (1040 min) | 1350-1440 (730-780) |
ARequires quenching and tempering. B9 CR steel is an air-hardenable steel, at times retaining austenite down to near atmospheric temperature. Good practice is to allow the steel to cool to 150° F or lower before subjecting the steel to a tempering treatment or post-weld heat treatment. |
Permissible Variations in Wall Thickness and Weight
Dictated by the requirements of the specification to which the manufacturer ordered the plate.
Permissible Variations in Outside Diameter
Based on circumferential measurement +/-0.5% of the specified outside diameter.
Umbrella 1 0 1 Cr2 Inches Equals
Reference documents
0.1 As A Fraction
ASTM A20/A20M Specification for General Requirements for Steel Plates for Pressure Vessels
ASTM A370 Test Methods and Definitions for Mechanical Testing of Steel Products
ASTM A387/A387M Specification for Pressure Vessel Plates, Alloy Steel, Chromium-Molybdenum
ASTM A435/A435M Specification for Straight-Beam Ultrasonic Examination of Steel Plates
ASTM A530/A530M Specification for General Requirements for Specialized Carbon and Alloy Steel Pipe
ASTM E165 Practice for Liquid Penetrant Examination for General Industry
ASTM E709 Guide for Magnetic Particle Testing
ASTM A204/A204M Specification for Pressure Vessel Plates, Alloy Steel, Molybdenum
ASTM A299/A299M Specification for Pressure Vessel Plates, Carbon Steel, Manganese-Silicon
ASTM A537/A537M Specification for Pressure Vessel Plates, Heat-Treated, Carbon-Manganese-Silicon Steel